LNP™ LUBRILOY™ RX99650 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AHtOXU_LNP-LUBRILOY-RX99650-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* RX99650 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRILOY* Compound PDX-R-99650 Product reorder name: RX99650 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 2.4 to 2.6 | % | |
| Across Flow : 24 hr | 2.4 to 2.6 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.73 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2220 | MPa | ASTM D638 |
| -- | 2160 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 60.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2 |
| Break | 53.1 | MPa | ASTM D638 |
| Break | 54.5 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.0 | % | ASTM D638 |
| Yield | 16 | % | ISO 527-2 |
| Break | 31 | % | ASTM D638 |
| Break | 64 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2080 | MPa | ASTM D790 |
| -- | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 80.7 | MPa | ASTM D790 |
| -- | 74.6 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.31 | ||
| vs. Itself - Static | 0.18 | ||
| Wear Factor - Washer | 8.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D256 |
| 23°C 2 | 19 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | No Break | ASTM D4812 | |
| 23°C 3 | 140 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 76.0 | J | ASTM D3763 |
| -- | 65.6 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 207 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 189 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 63.9 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 67.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.2E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3728 TRN700 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SITRAMAC 5E-IM-UV / C14/6 satine | SITRAPLAS GmbH | Acrylic (PMMA) | SITRAMAC |
| CERTENE™ HI-7053 | Muehlstein | HDPE | CERTENE™ |
| Chemlon® 109 U | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| LUVOCOM® 1850/CF/10/GF/10/GK/10/GS/5/FR | Lehmann & Voss & Co. | PBT | LUVOCOM® |