GLAMIDE® NB-5620S
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AHMGzw_GLAMIDE-NB-5620S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GLAMIDE®NB-5620S is a polyamide product that contains 15% mineral fillers. It is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.17 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 8.0 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.60 - 0.80 | -- | % | ASTM D955 |
| 3.00 mm | 1.4 - 1.8 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 0.50 | -- | % | ASTM D570 |
| Equilibrium, 65% RH | 2.1 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 100 | 90.0 | MPa | ASTM D638 |
| Yield, 23°C | 60.0 | 52.0 | MPa | ASTM D638 |
| Yield, 80°C | 25.0 | 22.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 8.0 | -- | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 6200 | 5400 | MPa | ASTM D790 |
| 23°C | 3700 | 2300 | MPa | ASTM D790 |
| 80°C | 2800 | 1400 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 160 | 152 | MPa | ASTM D790 |
| Yield, 23°C | 95.0 | 79.0 | MPa | ASTM D790 |
| Yield, 80°C | 40.0 | 30.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 40 | 60 | J/m | ASTM D256 |
| 23°C | 54 | 220 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 180 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 102 | -- | °C | ASTM D648 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 25 | 21 | kV/mm | ASTM D149 |
| Arc Resistance | 130 | 120 | sec | ASTM D495 |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Comparative Tracking Index, IEC Method: >600 V |
| 调节后的 Comparative Tracking Index, IEC Method: >600 V |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 240 - 290 | °C | |
| Mold Temperature | 50.0 - 120 | °C | |
| Injection Pressure | 50.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sungbo HI-LENE SBPS | Sungbo Co., Ltd. | TP, Unspecified | Sungbo |
| COSMOPLENE® AZ564 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Copolymer | COSMOPLENE® |
| Sylvin 3220-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| OnForce™ LFT AM-60LGF/001 BLACK | PolyOne Corporation | PPA | OnForce™ LFT |
| LNP™ THERMOCOMP™ DX06410 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |