RTP 2505

Category: PC+ABS , Polycarbonate + ABS
Manufacturer: RTP Company
Trademark: RTP
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: AGY8Pv_RTP-2505.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Glass Fiber
General Information
Filler / Reinforcement
  • Glass fiber reinforced material, 30% filler by weight
RoHS Compliance
  • Contact manufacturer
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.38g/cm³ASTM D792
Molding Shrinkage - Flow (3.20 mm)0.050 - 0.20%ASTM D955
Moisture Content 0.020%
Additional InformationNominal ValueUnit
Primary Additive 30%
MechanicalNominal ValueUnitTest Method
Tensile Modulus 9650MPaASTM D638
Tensile Strength 114MPaASTM D638
Tensile Elongation (Yield)2.0 - 3.0%ASTM D638
Flexural Modulus 8960MPaASTM D790
Flexural Strength 172MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (3.20 mm)110J/mASTM D256
Unnotched Izod Impact (3.20 mm)590J/mASTM D4812
FlammabilityNominal ValueTest Method
Flame Rating (1.50 mm, ** Values per RTP Company testing.)HBUL 94
InjectionNominal ValueUnit
Drying Temperature 93.3°C
Drying Time 4.0hr
Dew Point -28.9°C
Processing (Melt) Temp 243 - 274°C
Mold Temperature 51.7 - 93.3°C
Injection Pressure 68.9 - 103MPa
Injection instructions
Desiccant Type Dryer Required.
Resin Grade Manufacturer Category Trademark
NILAMID® B3 GCF2006 Nilit Plastics Nylon 6 NILAMID®
Chemlon® 100 XH Teknor Apex Company (Chem Polymer) Nylon 66 Chemlon®
Iupital® FX-11 Mitsubishi Engineering-Plastics Corp Acetal (POM) Copolymer Iupital®
KEBAFORM® C 90 M BARLOG plastics GmbH Acetal (POM) Copolymer KEBAFORM® C
LNP™ LUBRICOMP™ KL004A compound SABIC Innovative Plastics Acetal (POM) Homopolymer LNP™ LUBRICOMP™