TRANSMARE® 19HNF30-0.001
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AGNgQP_TRANSMARE-19HNF30-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 19HNF30-0.001 is a 30% bamboo fibre reinforced polypropylene homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 4.0 | g/10 min | |
| 190°C/5.0 kg | 14 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm) | 3700 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 4.00 mm) | 44.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 4.00 mm) | 2.5 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3700 | MPa | ISO 178 |
| Flexural Stress 2 | 61.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C | 2.2 | kJ/m² | |
| -20°C | 2.2 | kJ/m² | |
| 0°C | 2.5 | kJ/m² | |
| 23°C | 3.2 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 2.5 | kJ/m² | |
| -20°C | 2.5 | kJ/m² | |
| 0°C | 2.7 | kJ/m² | |
| 23°C | 3.4 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 160 | °C | ISO 306/A50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 165 | °C | |
| Middle Temperature | 175 | °C | |
| Front Temperature | 185 | °C | |
| Nozzle Temperature | 190 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-12362 | Teknor Apex Company | TPE | Medalist® |
| Mirakutoran® TPU P485 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| CONTINUUM™ DGDB-2490 NT | The Dow Chemical Company | HDPE | CONTINUUM™ |
| Hanwha Total PP TB71W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Braskem PE HD3000N | Braskem IDESA | HDPE | Braskem PE |