LNP™ STAT-KON™ FX98500C compound
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AFiIXb_LNPSTATKONFX98500Ccompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON FX98500C is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-F-98500 Product reorder name: FX98500C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.976 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 2.0 - 4.0 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.0 - 4.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 2.0 - 4.0 | % | ISO 294-4 |
| Flow direction : 24 hours | 2.0 - 4.0 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1080 | MPa | ASTM D638 |
| -- | 871 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 23.9 | MPa | ASTM D638 |
| Yield | 23.0 | MPa | ISO 527-2 |
| Fracture | 13.9 | MPa | ASTM D638 |
| Fracture | 14.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 16 | % | ASTM D638 |
| Yield | 14 | % | ISO 527-2 |
| Fracture | 43 | % | ASTM D638 |
| Fracture | 83 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 870 | MPa | ASTM D790 |
| -- | 931 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 26.5 | MPa | ASTM D790 |
| -- | 27.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 2 | 5.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 21.4 | J | ASTM D3763 |
| -- | 63.2 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 46.7 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 3 | 48.0 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 - 1.0E+5 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 - 204 | °C | |
| Middle Temperature | 210 - 221 | °C | |
| Front Temperature | 221 - 232 | °C | |
| Processing (Melt) Temp | 232 | °C | |
| Mold Temperature | 37.8 - 54.4 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 FR MS | RTP Company | Nylon 66 | RTP |
| TECOLITE KM-50BD | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| Ketron® PEEK-CLASSIX LSG | Quadrant Engineering Plastic Products | PEEK | Ketron® |
| PIVINEL™ 218-UV | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |
| Polychim HC10XC | Polychim Industrie S.A.S. | PP Homopolymer | Polychim |