Miramid® DK2520CW
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Leuna GmbH |
| Trademark: | Miramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AEZ1e1_Miramid-DK2520CW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Miramid® DK2520CW is a Polyamide 6 (Nylon 6) material filled with 20% glass fiber and 25% mineral. It is available in Europe for injection molding. Important attributes of Miramid® DK2520CW are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1520 | -- | kg/m³ | ISO 1183 1 |
| Water Absorption | ISO 62 2 | |||
| Saturation | 4.5 | -- | % | |
| Equilibrium | 1.4 | -- | % | |
| Viscosity number | 145 | -- | cm³/g | ISO 307, 1157, 1628 3 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 250 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile modulus | 9900 | 6100 | MPa | ISO 527-2 4 |
| Tensile Stress (Break) | 140 | 90.0 | MPa | ISO 527-2 5 |
| Tensile Strain (Break) | 2.0 | 5.0 | % | ISO 527-2 6 |
| Flexural Stress 7 | 210 | 140 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 8 | |||
| -30°C | 3.00 | -- | kJ/m² | |
| 23°C | 4.00 | 5.00 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 9 | |||
| -30°C | 35.0 | -- | kJ/m² | |
| 23°C | 45.0 | 50.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 10 | |||
| 0.45 MPa | 215 | -- | °C | |
| 1.8 MPa | 205 | -- | °C | |
| Continuous Use Temperature | ISO 2578 | |||
| -- 11 | 125 | -- | °C | |
| -- 12 | 140 | -- | °C | |
| -- 13 | 180 | -- | °C | |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume resistivity | 1.0E+13 | 1.0E+10 | ohms·m | IEC 60093 14 |
| Dielectric Constant (1 MHz) | 3.90 | 6.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.20 | IEC 60250 15 | |
| Comparative tracking index | 400 | -- | IEC 60112 16 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.50 mm) | HB | -- | UL 94 | |
| Burning Behav. at thickness h (1.50 mm) | HB | -- | ISO 1210 17 | |
| Glow Wire Flammability Index (1.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Typical values for uncoloured product at 23°C and 50% relative humidity |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Temperature index at loss of 50% tensile strength, 20000h |
| 12 . | Temperature index at loss of 50% tensile strength, 5000h |
| 13 . | Short time |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C ZH450 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Vyncolit® TEM 9010 | Vyncolit N.V. | Epoxy | Vyncolit® |
| Crastin® S600F40 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| ELEVATE™ EF529 | Westlake Chemical Corporation | EVA | ELEVATE™ |
| Petrothene® GS710060 | LyondellBasell Industries | LLDPE | Petrothene® |