LNP™ STAT-KON™ PE002 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ADxQmD_LNP-STAT-KON-PE002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON PE002 is a compound based on Nylon 6 resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PC-1002 Product reorder name: PE002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 1.18 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.30 to 0.50 0.30 to 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 to 0.80 0.60 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.74 0.74 | % | ISO 294-4 |
| Flow : 24 hr | 0.41 0.41 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 1.0 1.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11700 11700 | MPa | ASTM D638 |
| -- | 8670 8670 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 114 114 | MPa | ASTM D638 |
| Break | 124 124 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 6.8 6.8 | % | ASTM D638 |
| Break | 8.1 8.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5520 5520 | MPa | ASTM D790 |
| -- | 7400 7400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 172 172 | MPa | ASTM D790 |
| -- | 185 185 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 64 | J/m | ASTM D256 |
| 23°C 2 | 5.5 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 120 120 | J/m | ASTM D4812 |
| 23°C 3 | 8.1 8.1 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 219 219 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 215 215 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 198 198 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 197 197 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 8.1E-5 8.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 8.0E-5 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.0E-5 4.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 3.9E-5 3.9E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3857CT | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Shandong Nylon A4TR04 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon, Unspecified | Shandong Nylon |
| BLUESTAR® PBT 201-G20202 | Nantong Zhonglan Engineering Plastics Co., Ltd. | PBT | BLUESTAR® |
| Delrin® 527UVE NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| ESENTTIA 03R45C | Polipropileno del Caribe S.A. | PP Random Copolymer | ESENTTIA |