PRE-ELEC® CP 1515
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ADXCMC_PRE-ELEC-CP-1515.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® CP 1515 is a carbon black filled conductive thermoplastic compound based on polyolefin copolymer. In addition to a low electrical resistivity. PRE-ELEC® CP 1515 has an excellent balance of mechanical properties and is easy to extrude. PRE-ELEC® CP 1515 has been developed especially for block-process foams. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 190°C/21.6 kg | 50 | g/10 min | ASTM D1238, ISO 1133 |
| 190°C/5.0 kg | 1.2 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.2 | % | ASTM D955 |
| Flow direction | 1.2 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A | 95 | ASTM D2240, ISO 868 | |
| Shaw D | 50 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 11.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 450 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 4.00 mm | 1100 | MPa | ASTM D790 |
| 4.00 mm | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -20°C 1 | 40 | kJ/m² | ASTM D256, ISO 179 |
| 23°C 2 | No Break | ISO 179, ASTM D256 | |
| Charpy Unnotched Impact Strength 3 | |||
| -20°C | No Break | ASTM D256, ISO 179 | |
| 2°C | No Break | ISO 179 | |
| 23°C | No Break | ASTM D256 | |
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ASTM D256 | |
| 23°C, 4.00 mm | No Break | ASTM D256 | |
| Notched Izod Impact 4 | ISO 180 | ||
| -20°C | No Break | ISO 180 | |
| 23°C | No Break | ISO 180 | |
| Unnotched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ASTM D256 | |
| 23°C, 4.00 mm | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength 5 | ISO 180 | ||
| -20°C | No Break | ISO 180 | |
| 23°C | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 35.0 | °C | ASTM D648B, ISO 75-2/Bf |
| Vicat Softening Temperature | 50.0 | °C | ISO 306/A50, ASTM D1525 6 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+3 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+2 | ohms·cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Cylinder Zone 5 Temp. | 200 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 200°C |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thick |
| 3 . | 4 mm thick |
| 4 . | 4 mm thick |
| 5 . | 4 mm thick |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Solef® 6012 | Solvay Specialty Polymers | PVDF | Solef® |
| TOTAL Polypropylene PPR 3221 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| ADENE GHQBG | A.D. Compound spa | PP Copolymer | ADENE |
| Beamset 271 | Arakawa Chemical Industries, Ltd. | Acrylic, Unspecified | Beamset |
| CLEARTUF ULTRA | M&G Gruppo Mossi & Ghisolfi | PET | CLEARTUF |