TechnoPet GF 30 2 0

Category:	PET , Polyethylene Terephthalate
Manufacturer:	TechnoCompound GmbH
Trademark:	TechnoPet
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ACvBdZ_TechnoPetGF3020.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

TechnoPet: Attractive and cost effective

The TechnoPet compound line contains non-reinforced, glass fiber reinforced, impact strength modified as well as UV stabilized compounds for outdoor use.

TechnoPet compounds offer these properties:

High stiffness

High thermal stability >220°C

Attractive surface

High dimensional stability

For these reasons they represent an extremely cost effective solution compared with other technical compounds.

Typical Applications

Automotive industry: e.g. as a substitute for PA, engine covers...

Electrical engineering: e.g. lamp holders: glass fiber reinforced, flame retardant, high stiffness; multiple power sockets: modified impact strength, high dimensional accuracy...

Household appliances: e.g. steam irons: thermally stabilized PET compounds...

Packaging/logistics: e.g. logistic systems: modified impact strength, structural stability and strength...

Mechanical engineering: castors, bearings, gears, guide slide bearings...

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Features	High Dimensional Stability Rigidity, high Insulation Thermal stability, good Good appearance
Uses	Packaging Gear Electrical/Electronic Applications Electrical appliances Application in Automobile Field Bearing

Physical	Nominal Value	Unit	Test Method
Density	1.62	g/cm³	ISO 1183
Molding Shrinkage ¹			ISO 2577
Transverse flow	1.1	%	ISO 2577
Flow	0.30	%	ISO 2577
Water Absorption			ISO 62
23°C, 24 hr	0.15	%	ISO 62
Saturated, 23°C	0.40	%	ISO 62
Viscosity Number (Reduced Viscosity)	63.0	ml/g	ISO 1628

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness ²	250	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	10500	MPa	ISO 527-2/1
Tensile Stress (Break)	160	MPa	ISO 527-2/5
Tensile Strain (Break)	2.0	%	ISO 527-2/5

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	9.0	kJ/m²	ISO 179/1eA
23°C	9.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	30	kJ/m²	ISO 179/1eU
23°C	30	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	220	°C	ISO 75-2/A
8.0 MPa, not annealed	130	°C	ISO 75-2/C
Vicat Softening Temperature	255	°C	ISO 306/B50
Melting Temperature ³	240	°C	ISO 11357-3
CLTE - Flow (23 to 80°C)	2.0E-5	cm/cm/°C	ISO 11359-2

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+14	ohms	IEC 60093
Volume Resistivity	> 1.0E+16	ohms·cm	IEC 60093
Dielectric Strength (1.00 mm)	33	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
100 Hz	4.80		IEC 60250
1 MHz	4.20		IEC 60250
Comparative Tracking Index (Solution A)	250	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (0.8 mm)	HB		UL 94
Glow Wire Flammability Index (2.0 mm)	750	°C	IEC 60695-2-12

Note Message
1 .	275°C / WZ 135 bzw. 100°C, 600 bar
2 .	358 N
3 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
Trexprene® A88BW	Mitsubishi Chemical Performance Polymers, Inc.	TPV	Trexprene®
ADDILENE J 110	ADDIPLAST	PP Copolymer	ADDILENE
ALTECH® PC A 1000/620 UV	ALBIS PLASTIC GmbH	PC	ALTECH® PC
INTEX® 131	Versalis S.p.A.	SBR, Emulsion	INTEX®
Lucent TPO TPO-1015	Lucent Polymers, Inc.	Polyolefin, Unspecified	Lucent TPO