| INVISTA's Novadyn™ DT/DI is made from monomers DYTEK® A diamine, purified terephthalic acid (PTA) and purified isophthalic acid (PIA). |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.18 | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) 1 | 17 to 59 | -- | g/10 min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.97 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Shore Hardness (Shore D) | 84 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | 3500 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 102 | 111 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield, 23°C | 7.0 | 6.3 | % | |
| Break, 23°C | 8.3 | 7.4 | % | |
| Flexural Modulus 2(23°C) | 2900 | 3200 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 128 | 143 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 2.2 | -- | kJ/m² | |
| 23°C | 5.5 | 4.8 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179 | |
| Notched Izod Impact Strength | ISO 180 | |||
| -40°C | 2.1 | -- | kJ/m² | |
| 23°C | 6.7 | 4.3 | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | No Break | 110 kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 134 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 122 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 4 | 145 | -- | °C | DSC |
| Vicat Softening Temperature | ||||
| -- | 143 | -- | °C | ISO 306/A50 |
| -- | 139 | -- | °C | ISO 306/A120 |
| -- | 136 | -- | °C | ISO 306/B50 |
| -- | 141 | -- | °C | ISO 306/B120 |
| Optical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Gloss | ISO 2813 | |||
| 20° | 115 | -- | ||
| 60° | 128 | -- | ||
| 85° | 107 | -- | ||
| Transmittance | 90.7 | -- | % | ASTM D1003 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Moisture Absorption - After conditioning 5 | -- | 3.8 | % | ISO 1110 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Rear Temperature | 260 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 285 | °C | |
| Mold Temperature | 80.0 | °C | |
| Back Pressure | 1.50 | MPa | |
| Screw Speed | 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 270°C to 300°C |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 20°C/min |
| 5 . | Conditioned at 70°C, 62% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® PXA 12400 | Tekni-Films, a div of Tekni-Plex | Film, Copolyester/PCTFE | TEKNIFLEX® |
| Devcon Epoxy Plus™ 25 | Devcon | Epoxy | Devcon |
| Glastic® 2450-15 | Glastic Corporation | Polyester, TS | Glastic® |
| LUVOCOM® 1850-7315 | Lehmann & Voss & Co. | PBT | LUVOCOM® |
| Sarlink® TPE ME-2685B (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |