Lupoy® SC2202
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ABifzz_Lupoy-SC2202.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Good Toughness, Good Impact, Chemical Resistance Application Moible Phone Housing |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 to 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 90.7 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 7.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 4510 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 147 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(0.45 MPa, Unannealed, 6.40 mm) | 144 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 280 to 295 | °C | |
| Middle Temperature | 285 to 305 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Nozzle Temperature | 290 to 305 | °C | |
| Processing (Melt) Temp | 295 to 315 | °C | |
| Mold Temperature | 100 to 140 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 18.6kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu RTV KE-44 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| DELPET™ 80EB | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |
| GLS Blends MS309 | GLS Polymers Pvt. Ltd. | PC+ABS | GLS Blends |
| ISPLEN® PG 370 AT | REPSOL | PP Homopolymer | ISPLEN® |
| Sylvin 9604-90 Blue 8432 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |