INTEGRAL™ 604
| Category: | Polyolefin, Unspecified , Polyolefin Adhesive Film |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | INTEGRAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ABZGyg_INTEGRAL-604.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INTEGRAL™ 604 Polyolefin Adhesive Film is a heat-activated adhesive film specifically formulated for bonding to copper on both sides of the film. It can also be used as a tie layer to bond two different substrates together. New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative. General Characteristics:
|
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 58 | µm | |
| Film Thickness - Recommended / Available | 1.0-2.5 mil (25-64 µ) | ||
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 58 µm | 151 | MPa | |
| 2% Secant, MD : 58 µm | 128 | MPa | |
| 1% Secant, TD : 58 µm | 163 | MPa | |
| 2% Secant, TD : 58 µm | 131 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 58 µm | 8.96 | MPa | |
| TD : Yield, 58 µm | 7.79 | MPa | |
| MD : Break, 58 µm | 21.4 | MPa | |
| TD : Break, 58 µm | 15.4 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 58 µm | 18 | % | |
| TD : Yield, 58 µm | 15 | % | |
| MD : Break, 58 µm | 400 | % | |
| TD : Break, 58 µm | 530 | % | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 58 µm | 200 | g | |
| TD : 58 µm | 310 | g | |
| Film Width | 406 to 1520 | mm | |
| Yield | |||
| 25.0 µm | 42.6 | m²/kg | |
| 58.5 µm | 18.8 | m²/kg | ASTM D4321 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Heat Activation Temperature | 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOMAMID® 6 NAT | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| Geon™ Vinyl Rigid Extrusion 87736 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| KOCETAL® GF302BK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Karina MBPEB WHITE -E 1000/3055-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ PFD04S compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ STAT-KON™ |