Epocast 1635 A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AAxoQe_Epocast-1635-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Description: Epocast® 1635-A/B syntactic compound is a two-component, high-performance material designed for refilling mis-drilled holes in composite parts. This aluminum filled, high-viscosity system exhibits outstanding compressive strength and dynamic fatigue resistance under load at elevated temperature. This product is qualified to BMS 5-28, Type 31. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- 1 | 1.70 | g/cm³ | ASTM D1622 |
| -- 2 | 1.80 | g/cm³ | ASTM D1622 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | |||
| 25°C 3 | 172 | MPa | ASTM D695 |
| 177°C 4 | 82.7 | MPa | ASTM D695 |
| 25°C 5 | 103 | MPa | ASTM D695 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 23 | ||
| Shelf Life | |||
| 4°C | 52 | wk | |
| 25°C | 26 | wk | |
| Thermoset Mix Viscosity | ASTM D2196 | ||
| 25°C 6 | > 100000 | cP | ASTM D2196 |
| 25°C 7 | > 50000 | cP | ASTM D2196 |
| 25°C 8 | > 300000 | cP | ASTM D2196 |
| Gel Time - 100 gms (25°C) | > 1.0 | hr | ASTM D2471 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Extrudability - 80 psig (25°C) | > 90.0 | g/min | BMS 5-28 |
| Lap Shear - etched al/al | ASTM D1002 | ||
| 25°C 9 | 10.3 | MPa | ASTM D1002 |
| 25°C 10 | 10.3 | MPa | ASTM D1002 |
| Weight Gain 11 | % | ASTM D543 | |
| Cure Schedule: Seven days at 77°F (25°C) or gel at 77°F (25°C) and cure 150 minutes at 200°F (93°C). |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | System |
| 3 . | after 2.5 hours @ 200°F |
| 4 . | after 2.5 hours @ 200°F |
| 5 . | after 7 days @ 77°F |
| 6 . | System |
| 7 . | Hardener |
| 8 . | Resin |
| 9 . | after 2.5 hours @ 200°F |
| 10 . | after 7 days @ 77°F |
| 11 . | Fluids: DI water, BMS 3-11 Ty IV Cl 1 Gr A hydraulic (Skydrol 500B), MIL-PRF-5606 hydraulic, TT-S-735 Ty III ref fuel |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nivionplast® A R306GY NAT | SO.F.TER. SPA | Nylon 66 | Nivionplast® A |
| ADDILENE H 220 T20 | ADDIPLAST | PP Homopolymer | ADDILENE |
| LNP™ KONDUIT™ PX13322 compound | SABIC Innovative Plastics Asia Pacific | Nylon 6 | LNP™ KONDUIT™ |
| PLUSTEK PA340S4 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| Sylvin 916VO-85 Brown 7406 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |