AZDEL™ C401-B01
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Azdel, Inc. |
| Trademark: | AZDEL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AAtGPO_AZDEL-C401-B01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AZDEL C401-B01 is a glass mat thermoplastic laminate based upon random oriented chopped fiber mat contained within polypropylene resin matrix. This composite material features high flow properties and a very homogeneous fiber distribution. This material is typically used for standard semi-structural thin wall applications and where good glass distribution into features such as ribs and bosses is desired. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5970 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 106 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.2 | % | ISO 527-2 |
| Flexural Modulus | 5520 | MPa | ISO 178 |
| Flexural Stress | 146 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact | ASTM D3763 | ||
| 4.00 mm, Energy at Peak Load | 10.0 | J | ASTM D3763 |
| 4.00 mm, Total Energy | 18.8 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 160 | °C | ASTM D648 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 4.6 | mm/min | ISO 3795 |
| Additional Information |
|---|
| Basis Weight, Internal Test Method: 0.9 lbs/ft²Filler Content by Weight(ashing), Internal Test Method: 40 %Multi-axial Impact Peak Force, ASTM D3763, 4mm: 558 lbsNotched Izod Impact, ISO 180, 23°C, 4mm: 469 J/mPoissons Ratio, ISO 527: 0.333Sheet Thickness, Internal Test Method: 142 milsSpecific Gravity, ASTM D792, Laminated: 1.17Specific Gravity, ASTM D792, Molded: 1.19 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POYAD PA211 | Pooya Polymer Tehran | Polyolefin, Unspecified | POYAD |
| Bergamid™ BG6600-8051 RS BK001 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Chiao Fu PA66 MD212LB30 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| DINALON® B2S25 V2-7035 | Grupo Repol | Nylon 6 | DINALON® |
| LEXAN™ LUX1832 resin | SABIC Innovative Plastics | PC | LEXAN™ |