| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® ETP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AAakPs_Alathon-ETP-H4837.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON H4837 is a high-flow "freezer" grade resin that exhibits enhanced cold temperature impact performance, enhanced processing, and thermal stability with good color and organoleptic properties. Typical applications are rigid food containers such as 4-, 5- and 6- quart ice cream containers that are produced in fast cycling multi-cavity stack molds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.948 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.61 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 40 | g/10 min | ASTM D1238 |
| Spiral Flow | 46.7 | cm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 827 | MPa | |
| 1% Secant | 663 | MPa | |
| Tensile Strength 2(Break) | 21.8 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 5.4 | % | ASTM D638 |
| Flexural Modulus 4 | ASTM D790 | ||
| -- | 1060 | MPa | |
| 1% Secant | 985 | MPa | |
| 2% Secant | 829 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 23 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | 360 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 63.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 121 | °C | ASTM D1525 |
| Peak Melting Temperature | 127 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 114 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMATOP HDPE 055952 | Amco Polymers | HDPE | PRIMATOP |
| NYLOY® UB-0010N-V G55N2N | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| Polifil® Nylon 730-13GF | The Plastics Group | Nylon 6 | Polifil® Nylon |
| DURACON® LW-02 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| VALOX™ SHF4320 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |