Category: | PP, Unspecified , Polypropylene |
Manufacturer: | Poly Plastic |
Trademark: | Armlen® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | A8tnNG_Armlen-PP-TM-40-1.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Armlen® PP TM 40-1 is a Polypropylene product filled with mineral. It is available in Europe. |
General Information | |
---|---|
Filler / Reinforcement |
|
Physical | Nominal Value | Unit | |
---|---|---|---|
Density | 1.24 | g/cm³ | |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.6 | g/10 min | |
Molding Shrinkage | 0.40 to 0.60 | % |
Mechanical | Nominal Value | Unit | |
---|---|---|---|
Tensile Stress (Yield) | 30.0 | MPa | |
Tensile Strain (Break) | 37 | % | |
Flexural Modulus (23°C) | 3700 | MPa | |
Flexural Stress | 45.0 | MPa |
Impact | Nominal Value | Unit | |
---|---|---|---|
Charpy Notched Impact Strength (20°C) | 3.0 | kJ/m² | |
Charpy Unnotched Impact Strength | |||
-40°C | 6.0 | kJ/m² | |
20°C | 20 | kJ/m² |
Thermal | Nominal Value | Unit | |
---|---|---|---|
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 125 | °C | |
1.8 MPa, Unannealed | 75.0 | °C | |
Melting Temperature | 164 | °C | |
CLTE - Flow (-20 to 110°C) | 6.0E-6 | cm/cm/°C |
Electrical | Nominal Value | Unit | |
---|---|---|---|
Volume Resistivity 1 | 1.0E+15 | ohms·cm |
Note Message | |
---|---|
1 . | Dry |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Radilon® BN 200 AS/2 | Radici Plastics | Nylon 6 | Radilon® |
Shandong PA6 FRGFPA6 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 6 | Shandong PA6 |
STERLENE™ BMU147 | R&P (Pte.) Ltd. | TPO (POE) | STERLENE™ |
Vi-Chem PVC VNC70-30I-504132-AGC | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
BMC T40(18) | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |