NORYL GTX™ GTX902 resin

Category:	PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon
Manufacturer:	SABIC Innovative Plastics
Trademark:	NORYL GTX™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	A8oAEm_NORYL-GTX-GTX902-resin.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
Unreinforced. Excellent chemical resistance and paintability. 312F (155C) HDT.

General Information
Features	Sprayable Good chemical resistance
Processing Method	Injection molding
Multi-Point Data	Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Compressive Stress vs. Strain (ASTM D695) Flexural DMA (ASTM D4065) Instrumented Impact (Energy) (ASTM D3763) Instrumented Impact (Load) (ASTM D3763) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.08	g/cm³	ASTM D792
Molding Shrinkage
Flow : 130°C, 1 hour	1.1 - 1.5	%	ASTM D955
Flow : 3.20mm	0.90 - 1.2	%	Internal method
Transverse flow : 3.20mm	0.80 - 1.1	%	Internal method
Water Absorption			ASTM D570
24 hr	0.40	%	ASTM D570
Equilibrium, 23°C	3.6	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	118		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹			ASTM D638
Yield	60.0	MPa	ASTM D638
Fracture	56.5	MPa	ASTM D638
Tensile Elongation ²			ASTM D638
Yield	9.0	%	ASTM D638
Fracture	52	%	ASTM D638
Flexural Modulus ³(100 mm Span)	2240	MPa	ASTM D790
Flexural Strength ⁴(Yield, 100 mm Span)	89.6	MPa	ASTM D790
Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel)	19.0	mg	ASTM D1044

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
-40°C	53	J/m	ASTM D256
-30°C	120	J/m	ASTM D256
23°C	270	J/m	ASTM D256
Unnotched Izod Impact			ASTM D4812
-40°C	3200	J/m	ASTM D4812
-30°C	3200	J/m	ASTM D4812
23°C	3200	J/m	ASTM D4812
Instrumented Dart Impact			ASTM D3763
-40°C, Energy at Peak Load	19.7	J	ASTM D3763
-30°C, Energy at Peak Load	36.0	J	ASTM D3763
23°C, Energy at Peak Load	46.1	J	ASTM D3763

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, unannealed, 6.40mm	156	°C	ASTM D648
1.8 MPa, unannealed, 6.40mm	128	°C	ASTM D648
Vicat Softening Temperature
--	233	°C	ASTM D1525 ⁵
--	232	°C	ASTM D1525 ⁶
CLTE - Flow (-20 to 150°C)	9.0E-5	cm/cm/°C	ASTM E831
RTI Elec	50.0	°C	UL 746
RTI Imp	50.0	°C	UL 746
RTI	50.0	°C	UL 746

Flammability	Nominal Value		Test Method
Flame Rating (1.50 mm)	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	93.3 - 107	°C
Drying Time	3.0 - 4.0	hr
Drying Time, Maximum	8.0	hr
Suggested Max Moisture	0.070	%
Suggested Shot Size	30 - 50	%
Rear Temperature	260 - 299	°C
Middle Temperature	266 - 299	°C
Front Temperature	271 - 299	°C
Nozzle Temperature	277 - 299	°C
Processing (Melt) Temp	277 - 299	°C
Mold Temperature	65.6 - 93.3	°C
Back Pressure	0.345 - 1.38	MPa
Screw Speed	20 - 100	rpm
Vent Depth	0.013 - 0.038	mm

Injection instructions
Minimum Moisture Content: 0.02 %

Note Message
1 .	Type 1, 50mm/min
2 .	Type 1, 50mm/min
3 .	2.6 mm/min
4 .	2.6 mm/min
5 .	标准 B (120°C/h), 载荷2 (50N)
6 .	速率 A (50°C/h), 载荷2 (50N)

Resin Grade	Manufacturer	Category	Trademark
RTP 1305 TFE 10	RTP Company	PPS	RTP
Maxelast® A9850	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
APEX® 79-B427D-21D-85	Teknor Apex Company	PVC, Flexible	APEX®
Infino EN-1052	SAMSUNG SDI CO., LTD.	PC	Infino
Styroflex® 2G66	INEOS Styrolution Group GmbH	SBC	Styroflex®