Hanwha Total PP TF400
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A8SQZP_Hanwha-Total-PP-TF400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TF400 is a polypropylene terpolymer with ethylene and butene comonomers. TF400 is used for heat seal layer of cast or oriented PP films. This grade is provides a wide range of heat seal temperature and good sealing performance due to homogeneous comonomer distribution. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 70 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 27.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 500 | % | ASTM D638 |
| Flexural Modulus 3 | 735 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Strength - MD | ASTM D882 | ||
| Yield, 30 µm | 19.6 | MPa | ASTM D882 |
| Break, 30 µm | 44.1 | MPa | ASTM D882 |
| Tensile Elongation - MD (Break, 30 µm) | 500 | % | ASTM D882 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 120 | °C | ASTM D1525 4 |
| Melting Temperature | 134 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm) | 1.6 | % | ASTM D1003 |
| Additional Information |
|---|
| Stiffness, SAMSUNG TOTAL: 0.15 g/15min |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® B 31101 | Reliance Industries Limited | HDPE | RELENE® |
| Alpha PVC GW 3035-VW1 NATURAL LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| apilon 52c® C 60 | API SpA | TPU-Polyester | apilon 52c® |
| Gallonprene® GP540-6505C | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Petroquim PP PH 0322 | Petroquim S.A. | PP Homopolymer | Petroquim PP |