Order Products : sales@su-jiao.com
GLS PP ZT49
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A7CMPR_GLS-PP-ZT49.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP 20TALC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 to 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 to 12 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 30.0 to 36.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2200 to 2400 | MPa | ASTM D790 |
| Flexural Strength | 34.0 to 36.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 30 to 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 75.0 to 78.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 78.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 32.0 to 64.0 | °C | |
| Injection Pressure | 65.0 to 105 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riteflex® 447 | Celanese Corporation | TPEE | Riteflex® |
| Tenac™-C TFC77 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Ultramid® A3EG3 | BASF Corporation | Nylon 66 | Ultramid® |
| Chemlon® HY2SM | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Hapflex™ 781 | Hapco Inc. | TP, Unspecified | Hapflex™ |