Order Products : sales@su-jiao.com
Ghaed ABS/PC GAC 265
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Ghaed Basir Petrochemicals Co. |
| Trademark: | Ghaed ABS/PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A79fqB_Ghaed-ABS-PC-GAC-265.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC/ABS Alloy : Non Reinforced Grade Classification: General purpose>Injection grade Characteristic: Injection grade, Ultra high impact Resistance Application GAC 265 resin gives exceptional impact strength even at low temperature and has a highheat resistance. Typical applications include automotive instrument panel, automotive interior and exteriortrim .This resin is particularly suited for thin wall molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/21.6 kg) | 30 to 40 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 to 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 23°C) | > 53.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C) | > 95 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | > 1860 | MPa | ASTM D790 |
| Flexural Strength 4(23°C) | > 78.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 5 | > 55 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 118 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 95.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 230 to 260 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 260 to 270 | °C | |
| Processing (Melt) Temp | 270 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 6.4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan 1006A/B-5009 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyether | Xuchuan |
| BONDYRAM® TL4101B | Polyram Ram-On Industries | PE, Unspecified | BONDYRAM® |
| Evoprene™ HP 3702 | AlphaGary | SBC | Evoprene™ HP |
| FHR EPS 54-7354 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| ICORENE® N4505 | ICO Polymers EMEA, A Division of A. Schulman | PP Random Copolymer | ICORENE® |