OmniCarb™ PC/PBT 400IM2 UV
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniCarb™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A79SwU_OmniCarb-PC-PBT-400IM2-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cold Temperature Impact Resistant, UV Stabilized, PC/PBT Alloy |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 to 1.1 | % | |
| Across Flow | 0.10 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 120 | % | ASTM D638 |
| Flexural Modulus | 1930 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 640 | J/m | |
| 23°C, 3.18 mm | 750 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 96.1 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, Black | HB | ||
| 3.00 mm, Black | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 116 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 227 to 243 | °C | |
| Middle Temperature | 232 to 249 | °C | |
| Front Temperature | 238 to 260 | °C | |
| Nozzle Temperature | 238 to 260 | °C | |
| Processing (Melt) Temp | 238 to 260 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA PS 3122 90/05 | MBA Polymers | PS (GPPS) | MBA PS |
| Rainmaker Polypropylene MCCPMI20 | Rainmaker Polymers LLC | PP Copolymer | Rainmaker Polypropylene |
| Shinblend® A724 | Shinkong Synthetic Fiber Corp. | PC+PBT | Shinblend® |
| ALFATER XL® D40E 1GP0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Hostacom PPU X9067HS C12470 | LyondellBasell Industries | PP Copolymer | Hostacom |