AKROMID® A3 1 FR natural (3028)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A5caiP_AKROMID-A3-1-FR-natural-3028-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 1 FR natural (3028) is an unreinforced, heat stabilised, halogen- free flame retardant polyamide 6.6 with light inherent color, listet at UL in all colors. Applications are switch parts and housings in the electric industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.18 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.1 | % | |
| Flow | 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 80.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | > 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3300 | MPa | ISO 178 |
| Flexural Stress 2 | 125 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 6.2 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 80 | kJ/m² | |
| 23°C | 85 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| Melting Temperature 4 | 260 | °C | DIN EN 11357-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength (3.00 mm) | 19 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.800 mm) | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prixene® EA003S56 | POLYMAT | HDPE | Prixene® |
| Mowital® B 45 M | Kuraray Co., Ltd. | PVB | Mowital® |
| Catalyst CT/2-LR | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| ARNYL PA66 NERO | Daloga srl | Nylon 66 | ARNYL |
| Clariant PBT PBT-1100G30TF15 | Clariant Corporation | PBT | Clariant PBT |