Infino FD-1010
| Category: | PC , Polycarbonate |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A5TsTo_InfinoFD1010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Infino FD-1010 is a polycarbonate (PC) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: lighting equipment. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 16 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.50 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.50 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.50 | % | ISO 2577 |
| Traffic : 3.20mm | 0.50 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 120 | ASTM D785 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2060 | MPa | ASTM D638 |
| -- | 2000 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 63.7 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 75.5 | MPa | ASTM D638 |
| Fracture | 65.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 100 | % | ASTM D638 |
| Fracture | 100 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2260 | MPa | ASTM D790 |
| -- 6 | 2260 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 94.1 | MPa | ASTM D790 |
| -- 8 | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 120 | J/m | ASTM D256 |
| 23°C 10 | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm | 139 | °C | ISO 75-2/B |
| 0.45 MPa, annealing, 4.00mm | 139 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 130 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 125 | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 4.00mm | 125 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 144 | °C | ISO 306/B50 |
| -- | 148 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 to 2.0mm | V-2 | UL 94 | |
| 3.0 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Hot air dryer | 100 | °C | |
| Drying Time | |||
| -- | 2.0 - 6.0 | hr | |
| Hot air dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 280 - 300 | °C | |
| Middle Temperature | 260 - 270 | °C | |
| Front Temperature | 240 - 250 | °C | |
| Nozzle Temperature | 290 - 310 | °C | |
| Mold Temperature | 40 - 100 | °C | |
| Injection Pressure | 49.0 - 245 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Modified LDPE | Quadrant Engineering Plastic Products | LDPE | Quadrant EPP |
| RTP 100 | RTP Company | PP, Unspecified | RTP |
| Monprene® OM-10270 | Teknor Apex Company | TPE | Monprene® |
| YUNGSOX® PP 5070 | Formosa Polypropylene | PP Random Copolymer | YUNGSOX® PP |
| NEFTEKHIM PS 945E | Nizhnekamskneftekhim Inc. | PS (HIPS) | NEFTEKHIM PS |