Rotec® ABS 1001 GK20
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Rotec® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A5GzO1_RotecABS1001GK20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Rotec®ABS 1001 GK20 is an acrylonitrile butadiene styrene (ABS) material containing 20% glass beads. This product is available in Europe, and the processing method is injection molding. Rotec®The main characteristics of ABS 1001 GK20 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 18 | g/10 min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 34.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 15 | % | ISO 527-2/5 |
| Flexural Modulus 1(23°C) | 2900 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 68.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene庐 CP-37154 | Teknor Apex Company | TPE | Monprene® |
| VESTAKEEP® Film 0FH81 | Evonik Industries AG | PEEK | VESTAKEEP® Film |
| AKROMID® B3 GF 30 2 GIT black (4618) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Lapex A | LATI S.p.A. | PESU | Lapex |
| Tenac™ 2013A | Asahi Kasei Corporation | Acetal (POM) Homopolymer | Tenac™ |