AMPLIFY™ TY 1354
| Category: | MAH-g , Functional Polymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AMPLIFY™ TY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A59MPo_AMPLIFY-TY-1354.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AMPLIFY™ TY 1354 Functional Polymer is a maleic anhydride grafted (MAH) polymer. In tie layers for flexible packaging, AMPLIFY TY 1354 Functional Polymer promotes adhesion of Polyethylene to barrier polymers such as polyamide and other polar substrates. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| MAH Graft Level 1 | Low | Internal method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Resistance (51 µm) | 9.51 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 214 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 240 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 11.2 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 11.5 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 35.2 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 31.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 730 | % | ASTM D882 |
| TD : Fracture, 51 µm | 750 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 210 | g | ASTM D1709 |
| Elmendorf Tear Strength 2 | ASTM D1922 | ||
| MD : 51 µm | 890 | g | ASTM D1922 |
| TD : 51 µm | 1100 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.9 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 123 | °C | Internal method |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 66 | ASTM D2457 |
| Extrusion instructions |
|---|
| Recommended Melt Temperature - 400-446°FFabrication Conditions for Blown Film Screw Size: 2.5 in. (63.5 mm); 24:1 L/D Screw Type: Barrier screw Die Gap: 70 mil (1.8 mm) Melt Temperature: 430°F (221°C) Output: 6 lb/hr/in of die circumference Die diameter: 6 in Blow-Up Ratio: 2.5:1 Screw Speed: 70 rpm |
| Note Message | |
|---|---|
| 1 . | Low: <0.25 wt%, Medium 0.25-0.5, High >0.5 wt% |
| 2 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toughblend® PP-1650 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP Copolymer | Toughblend® |
| Unichem 8990 | Colorite Polymers | PVC, Unspecified | Unichem |
| ESENTTIA 60C90ND | Polipropileno del Caribe S.A. | PP Impact Copolymer | ESENTTIA |
| HiFill FR® PA6 FR-N | Techmer Engineered Solutions | Nylon 6 | HiFill FR® |
| ESTOPLAST EP 4130GN05 | Ester Industries Ltd. | PBT | ESTOPLAST EP |