RTP ESD 1384
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A4aYyv_RTP-ESD-1384.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbon Fiber - Electrically Conductive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.020 to 0.080 | % | ASTM D955 |
| Moisture Content | 0.040 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay | < 0.5 | sec | FTMS 101C 4046.1 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 25 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 24800 | MPa | ASTM D638 |
| Tensile Strength | 186 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 0.50 to 1.0 | % | ASTM D638 |
| Flexural Modulus | 20000 | MPa | ASTM D790 |
| Flexural Strength | 241 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 330 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 268 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | < 1.0E+4 | ohms | ASTM D257 |
| -- | < 1.0E+3 | ohms | ESD STM11.11 |
| Volume Resistivity | < 1.0E+2 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 307 to 329 | °C | |
| Mold Temperature | 135 to 177 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® PM-9640 (Compression) | Sumitomo Bakelite North America, Inc. | Phenolic | Sumikon® |
| Vinnolit® MP 6852 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| Wellamid® GF33-66 XE-N1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| AKROMID® B3 GF 30 S1 white (3767) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Panlite® B-8130R | TEIJIN LIMITED | PC | Panlite® |