HiFill® ABS GF 15 BK
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A3kFMM_HiFill-ABS-GF-15-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® ABS GF 15 BK is an Acrylonitrile Butadiene Styrene (ABS) product filled with 15% glass fiber. It can be processed by injection molding and is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.15 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.13 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 93.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 6000 | MPa | ASTM D790 |
| Flexural Strength | 123 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 350 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 112 | °C | |
| 1.8 MPa, Unannealed | 103 | °C | |
| CLTE - Flow | 3.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 18 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 to 87.8 | °C | |
| Drying Time | 2.0 to 16 | hr | |
| Rear Temperature | 216 to 232 | °C | |
| Middle Temperature | 221 to 238 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Nozzle Temperature | 199 to 221 | °C | |
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 71.1 to 87.8 | °C |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® P50 FIBK | Nilit Plastics | Nylon 66 | POLYNIL® |
| 4PROP® 9C22430 | 4Plas | PP Copolymer | 4PROP® |
| KPOL-NYLON K-NY6/27B | KPOL Chem Co. | Nylon 6 | KPOL-NYLON |
| LG PVC PB900 | LG Chem Ltd. | PVC Homopolymer | LG PVC |
| Zetpol® 2020L | Zeon Corporation | NBR | Zetpol® |