INEOS LLDPE LL3910AA
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A3a06h_INEOS-LLDPE-LL3910AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LLDPE film products Applications: LL3910AA is particularly suitable for use in lean and rich blend blown film applications, such as overwrap, counter bags, shrink film (lean blends, 10 to 30% LLDPE) and boil-in-the-bag applications. Benefits and Features: LL3910AA is a linear low density polyethylene copolymer containing hexene-1 as the comonomer. It offers the following properties:
If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. We recommend that you consult your INEOS technical representative for further advice on the use of LL3910AA. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.936 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) 2(190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Modulus - 1% Secant (38 µm, Blown Film) | 450 | MPa | ISO 1184 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 38 µm, Blown Film | 18.0 | MPa | |
| TD : Yield, 38 µm, Blown Film | 21.0 | MPa | |
| MD : Break, 38 µm, Blown Film | 54.0 | MPa | |
| TD : Break, 38 µm, Blown Film | 36.0 | MPa | |
| Tensile Elongation | ISO 1184 | ||
| MD : Break, 38 µm, Blown Film | 780 | % | |
| TD : Break, 38 µm, Blown Film | 990 | % | |
| Dart Drop Impact (38 µm, Blown Film) | 65 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 35 | g | |
| TD : 25 µm, Blown Film | 330 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 121 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 13 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Conditioned according to ISO 1872/1 |
| 2 . | Condition 4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIBUR Synthetic Rubber BR-1203 Ti Grade A | SIBUR, LLC | PBR, High Cis | SIBUR Synthetic Rubber |
| Epoxies, Ect. 10-3062 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| ESPRENE EPDM 512F | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| LNP™ LUBRILOY™ D2000P compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |
| Sylvin 8980-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |