LEXAN™ LGK3020 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A2YgEp_LEXAN-LGK3020-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass reinforced. Flame retardant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.050 to 0.25 | % | |
| Across Flow : 3.20 mm | 0.15 to 0.35 | % | |
| Water Absorption (24 hr) | 0.13 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 118 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 6580 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 148 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 146 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.7E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.7E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.20 mm, in Oil) | 18 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 293 to 316 | °C | |
| Middle Temperature | 304 to 327 | °C | |
| Front Temperature | 316 to 338 | °C | |
| Nozzle Temperature | 310 to 332 | °C | |
| Processing (Melt) Temp | 316 to 338 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SD101G30 | RJM International, Inc. | PC | RJM |
| Nypol® PA A3 G35 HS UV RH PRTA010 NR346 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| EcoLon® MRGF1878-BK1 | Wellman Engineering Resins | Nylon 6 | EcoLon® |
| MAJORIS EE097 - 7803 | AD majoris | PP, Unspecified | MAJORIS |
| POLYfill PP EIP5025 F | Polykemi AB | PP+EPDM | POLYfill |