PROTEQ™ C30UST5LS
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | PROTEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A2F3oo_PROTEQ-C30UST5LS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PROTEQ™ C30UST5LS is a high impact, high melt flow polypropylene copolymer containing 25% talc filler. It features improved heat ageing and UV performance, good fluidity and optimal balance between toughness and regidity. The grade also contains antistatic additives. ProteQ C30UST5LS is designed for various automotives interior applications such door trim and instrument panel. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.85 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 71 | ||
| Shore D, 15 sec | 64 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 23.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 90 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 36.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 250 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 122 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 68.0 | °C | |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 195 to 215 | °C | |
| Middle Temperature | 205 to 225 | °C | |
| Front Temperature | 215 to 235 | °C | |
| Processing (Melt) Temp | 220 to 270 | °C | |
| Mold Temperature | 30.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P26SRNAT | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| TEKAMID™ TA250G15 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Zislloy® BFG30-BN00N2 | Zig Sheng Industrial Co., Ltd. | Nylon 6 | Zislloy® |
| AMTOPP BA30 | Inteplast Group | PP, Unspecified | AMTOPP |
| O'Tech OW 939 PLTC | O'Tech Corporation | PVC, Unspecified | O'Tech |