Zytel® RS LC1610 BK387
| Category: | Nylon 1010 , RENEWABLY SOURCED™ POLYAMIDES* |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® RS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A27gKb_Zytel-RS-LC1610-BK387.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plasticized, Toughened, Renewably Sourced, Polyamide 1010 Developed for Extrusion |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.05 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 1.6 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 1.5 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.75 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 790 | 570 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 35.0 | 33.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 32 | 39 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | > 50 | % | ISO 527-2 |
| Flexural Stress | ISO 178 | |||
| 3.5% Strain | 24.0 | 19.0 | MPa | |
| -- | 24.0 | 19.0 | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | 6.0 | kJ/m² | |
| 23°C | 24 | 34 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 6.0 | 5.5 | kJ/m² | |
| 23°C | 24 | 35 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 110 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 46.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 197 | -- | °C | ISO 11357-3 |
| Freezing Point 2 | 175 | -- | °C | ISO 11357 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Viscosity (250°C, 1000 sec^-1) | 210 | -- | Pa·s | ISO 11443 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M2500CD (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| VENELENE® 11U4 | Poliolefinas Internacionales, C.A. (Polinter) | LLDPE | VENELENE® |
| Evermore PUR SS-1338N | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Elastron® G G601.A95.B | Elastron USA, Inc. | SEBS | Elastron® G |
| LIHAN® B801 | Nanjing Lihan Chemical Co., Ltd. | Nylon 6 | LIHAN® |