CALIBRE™ 201-10
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A1ugbo_CALIBRE-201-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 201-10 is produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. It provides excellent impact resistance, heat distortion resistance and optical clarity. CALIBRE 201-10 product is formulated with mold release. Govt. and Industry Standards:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.20 | g/cm³ | ISO 1183/A |
| -- | 1200 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ISO 1133 |
| Melt volume-flow rate (300°C/1.2 kg) | 8.00 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/50, ISO 527-2 3 3 |
| Tensile Stress | |||
| Yield | 60.0 | MPa | ISO 527-2/50, ISO 527-2 4 |
| Break | 71.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 6.0 | % | ISO 527-2/50, ISO 527-2 5 |
| Break | 150 | % | ISO 527-2/50 |
| Nominal strain at break | > 50 | % | ISO 527-2 6 |
| Flexural Modulus 7 | 2400 | MPa | ISO 178 |
| Flexural Stress 8 | 97.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 9 | ||
| -30°C | 13.0 | kJ/m² | |
| 23°C | 90.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 10 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength (23°C) | 88 | kJ/m² | ISO 180/4A |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 144 | °C | ISO 75-2/B |
| 0.45 MPa | 145 | °C | ISO 75-2 11 |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 141 | °C | ISO 75-2/A |
| 1.8 MPa | 131 | °C | ISO 75-2 12 |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ISO 306/B50 |
| 50°C/h, B (50N) | 149 | °C | ISO 306 13 |
| Ball Indentation Temperature | 125 | °C | IEC 60335-1 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 14 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume resistivity | > 1.0E+13 | ohms·m | IEC 60093 15 |
| Electric strength | 17 | kV/mm | IEC 60243-1 16 |
| Relative Permittivity | IEC 60250 17 | ||
| 100 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 18 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 | ||
| Comparative Tracking Index (2.00 mm) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 19 | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm, UL) | HB | ISO 1210 20 | |
| Burning Behav. at thickness h (3.20 mm, UL) | HB | ISO 1210 21 | |
| Oxygen index | 26 | % | ISO 4589-2 22 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 87.0 to 91.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | 2.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 22 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2923-67LG Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Vipel® K022-ACA-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| TUFNYL® SFRO NATURAL | SRF Ltd. | Nylon 6 | TUFNYL® |
| Yuyao PET PET126 | Yuyao Tenglong Plastics Co., Ltd. | PET | Yuyao PET |
| INEOS HDPE J50-1000-187 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |