Delrin® FG500MP NC010
| Category: | Acetal (POM) Homopolymer , ACETAL RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Delrin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A0drkH_DelrinFG500MPNC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Teflon® Lubricated Medium Viscosity Acetal Homopolymer |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.6 | % | ISO 294-4 |
| Flow | 1.9 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 12 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 17 | % | ISO 527-2 |
| Flexural Modulus | 3200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 120 | kJ/m² | ISO 179/1eU |
| 23°C | 130 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 163 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 100 | °C | ISO 75-2/A |
| Melting Temperature 1 | 178 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | mm/min | ISO 3795 |
| Flammability Classification (1.5 mm) | HB | IEC 60695-11-10, -20 | |
| FMVSS Flammability | B | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 215 | °C | |
| Mold Temperature, Optimum | 90 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 8.00 | s/mm | |
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 210 - 220 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Holding Pressure | 80.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HMN TR-938 | Chevron Phillips Chemical Company LLC | MDPE | Marlex® |
| 3M™ Dyneon™ Fluoroplastic PFA 6502NZ | 3M Advanced Materials Division | PFA | 3M™ Dyneon™ Fluoroplastic |
| CompaDur® 121 GF 30 FR black (041) | DimeLika Plast GmbH | PBT | CompaDur® |
| Hapweld™ 37 | Hapco Inc. | TP, Unspecified | Hapweld™ |
| LUVOCOM® 1-0936-3 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |