Iupiace® EHM1000 9905M
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupiace® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A0Vmh2_Iupiace-EHM1000-9905M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Iupiace® EHM1000 9905M is a Polyphenylene Ether + PS (PPE+PS) material. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Iupiace® EHM1000 9905M: Antistatic. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.70 to 0.90 | % | |
| Flow : 3.20 mm | 0.70 to 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 9.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 102 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 100 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 161 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 290 to 310 | °C | |
| Middle Temperature | 310 to 330 | °C | |
| Front Temperature | 310 to 330 | °C | |
| Nozzle Temperature | 310 to 330 | °C | |
| Mold Temperature | 110 to 130 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermylene® P6-25FG-0687 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| VALOX™ 315 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |
| DINAPLEN® PPH1S15 G30 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| FMC® 200 | Smooth-On, Inc | Polysulfide Rubber | FMC® |
| Silastic® 7-6830 | Dow Corning Corporation | Silicone | Silastic® |