AMPLIFY™ GR 204
| Category: | MAH-g , Functional Polymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AMPLIFY™ GR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A0Gywk_AMPLIFY-GR-204.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AMPLIFY™ GR 204 Functional Polymer is a maleic anhydride grafted (MAH) polymer concentrate designed as a blend component for unmodified polyethylene. AMPLIFY GR 204 Functional Polymer promotes adhesion of polyethylene to polyamide and ethylene vinyl alcohol (EVOH). The functionality of this polymer also promotes adhesion between metal, polyolefins, cellulose, polyester, polycarbonate, glass, and foil. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| MAH Graft Level 1 | Very high | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A | 97 | ASTM D2240, ISO 868 | |
| Shaw D | 64 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture 2 | 16.0 | MPa | ASTM D638 |
| Fracture | 16.0 | MPa | ISO 527-2/51 |
| Tensile Elongation | |||
| Fracture 3 | 100 | % | ASTM D638 |
| Fracture | 100 | % | ISO 527-2/51 |
| Flexural Modulus - 2% Secant | 786 | MPa | ASTM D790A, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 121 | °C | ASTM D1525, ISO 306 |
| Melting Temperature (DSC) | 127 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D4976 进行模塑。 |
| Note Message | |
|---|---|
| 1 . | Low:<0.25 wt%, medium 0.25-0.5, high> 0.5 wt%, very high> 1.0 wt% |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 1965N0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| SCANAMID 66 A12^ X30 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Starglas FX05032 | Eurostar Engineering Plastics | PE, Unspecified | Starglas |
| INSPIRE™ TF4700SZ | Trinseo | PP, Unspecified | INSPIRE™ |
| Sylvin 6034-85 Clear Yellow 4112 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |