Eltex® PF6112AA is a metallocene LLDPE resin produced in Europe.

Benefits and Features
Eltex® PF6112AA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It is a very high toughness material offering the following properties:

Unrivalled impact strength

Excellent puncture resistance

Superior optical properties

Very good bubble stability and extrudability similar to the best LLDPE blown film grades

Low temperature sealing characteristics

Applications
Eltex® PF6112AA has been developed for use in food packaging and other thin film applications where superior mechanical and optical performance is required. It is also particularly suitable for relatively thick film applications requiring superior mechanical strength and easy sealing like liners for containers and silos. In addition, Eltex® PF6112AA offers easy extrudability.

In multilayer films, Eltex® PF6112AA can be used neat or as a blending partner with LLDPE or LDPE.

General Information
Additive	Antioxidation
Features	Ultra-high impact resistance Ultra high toughness Low density Low temperature heat sealability Copolymer Optical hexene comonomer Perforation resistance Antioxidation Workability, good Compliance of Food Exposure
Uses	Films Lining Multilayer film Mixing Food packaging
RoHS Compliance	Contact manufacturer
Forms	Particle
Processing Method	Film extrusion Extrusion

Physical	Nominal Value	Unit	Test Method
Density (23°C)	0.916	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.3	g/10 min	ISO 1133

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
Tensile Modulus			ISO 527-3
1% secant, MD : 25 µm, blown film	155	MPa	ISO 527-3
1% secant, TD : 25 µm, blown film	160	MPa	ISO 527-3
Tensile Stress			ISO 527-3
MD : Yield, 25 µm, blown film	10.0	MPa	ISO 527-3
TD : Yield, 25 µm, blown film	10.0	MPa	ISO 527-3
MD : Broken, 25 µm, blown film	65.0	MPa	ISO 527-3
TD : Broken, 25 µm, blown film	60.0	MPa	ISO 527-3
Tensile Elongation			ISO 527-3
MD : Broken, 25 µm, blown film	590	%	ISO 527-3
TD : Broken, 25 µm, blown film	660	%	ISO 527-3
Dart Drop Impact (25 µm, Blown Film)	> 1700	g	ASTM D1709A
Elmendorf Tear Strength			ASTM D1922
MD : 25 µm, blown film	220	g	ASTM D1922
TD : 25 µm, blown film	420	g	ASTM D1922

Thermal	Nominal Value	Unit	Test Method
Melting Temperature (DSC)	101 - 116	°C	Internal method

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 25.0 µm, Blown Film)	70		ASTM D2457
Haze (25.0 µm, Blown Film)	5.0	%	ASTM D1003

Resin Grade	Manufacturer	Category	Trademark
Tislamid® PA6 PA6 25 GFR FR	Tisan	Nylon 6	Tislamid® PA6
CP PRYME® Nylon 66 NN102MD	Chase Plastics Services Inc.	Nylon 66	CP PRYME® Nylon 66
FERREX® GPP20CS88HB	Ferro Corporation	PP Copolymer	FERREX®
Elasthane™ 75D	DSM Biomedical Inc.	TPU-Polyether	Elasthane™
KOPLA PA6 KNP1000F	KOPLA Co., Ltd.	Nylon 6	KOPLA PA6