Hostalen CRP 100 RT black
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9zqEgL_Hostalen-CRP-100-RT-black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen CRP 100 RT black is a high density polyethylene (HDPE), black coloured similar RAL 9004, with high melt viscosity for extrusion, injection and compression moulding. The product is used by customers in pipe and sheet applications and provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength even at raised temperature (RT). It has an excellent heat ageing and extremely high extraction stability. It is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.957 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 9.5 | g/10 min | |
| 190°C/5.0 kg | 0.45 | g/10 min | |
| Carbon Black Content | 2.3 | % | ISO 6964 |
| Full Notch Creep Test (80°C) 1 | 14.6 | day |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Creep Modulus 2 | DIN 19537-2 | ||
| 1 min | 1.00 | GPa | |
| 2000 hr | 0.300 | GPa | |
| 24 hr | 0.470 | GPa |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Elongation - TD | > 350 | % | EN 638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (210°C) | 40 | min | ISO 11357-6 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Odor Threshold | < 2.00 | EN 1622/EN 1420 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 59 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1050 | MPa | ISO 527-2/50 |
| Tensile Stress (Yield, 23°C) | 22.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 8.0 | % | |
| Break, 23°C, 4.00 mm | 600 | % | |
| Tensile Creep Modulus 3 | ISO 899-1 | ||
| 1 hr | 640 | MPa | |
| 1000 hr | 300 | MPa | |
| Flexural Stress (3.5% Strain) | 18.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 24 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 70.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 200 to 280 | °C |
| Note Message | |
|---|---|
| 1 . | 4.0 MPa, 2% Arkopal N 100 |
| 2 . | 4 point loading method |
| 3 . | 2.0 MPa load |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® EME-7720R | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| AVP™ RLL20CP | SABIC Innovative Plastics | PC | AVP™ |
| DENKA STYROL MF-21-301 | Denka Company Limited | PS (GPPS) | DENKA STYROL |
| POLYFLON™ LDW-40 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |
| Sylvin 6168-80 Red 6204 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |