Lupox® NH2306F
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupox® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9zk8CS_Lupox-NH2306F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Halogen Free Flame Retardant Application IT/OA, E&E(Connector) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 1.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 98.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 8830 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 162 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 210 | °C | ASTM D648 |
| Peak Melting Temperature | 223 | °C | ASTM D3418 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) 5 | PLC 0 | UL 746 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 240 to 245 | °C | |
| Middle Temperature | 245 to 250 | °C | |
| Front Temperature | 250 to 255 | °C | |
| Nozzle Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 250 to 265 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-34445 NAT XRD1 | Teknor Apex Company | TPE | Medalist® |
| Sylvin 8672-60 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Lumid® HI1202A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |
| PLUSTEK PB145 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| POLYFORT® FPP 1005 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |