KumhoSunny PBT/ABS HAB8740
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PBT/ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9yURMV_KumhoSunny-PBT-ABS-HAB8740.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HAB8740 is a high flow and high Impact PBT/ABS alloy resin, offering medium heat resistance,excellent normal and low temperature impact strength and chemical resistance.HAB8740 is recommended for automobile parts, office appliance, electrical and electronic components. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 | g/cm³ | ASTM D792 |
| -- | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 250°C/5.0 kg | 20 | g/10 min | ASTM D1238 |
| 260°C/5.0 kg | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 to 0.80 | % | ASTM D955 |
| -- | 0.50 to 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 47.0 | MPa | ASTM D638 |
| -- | 50.0 | MPa | ISO 527-2/5 |
| Tensile Elongation (Break) | 150 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 1700 | MPa | ASTM D790 |
| -- 1 | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 65.0 | MPa | ASTM D790 |
| -- 2 | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 23 | kJ/m² | |
| 23°C | 48 | kJ/m² | |
| Notched Izod Impact | |||
| 3.20 mm | 700 | J/m | ASTM D256 |
| 23°C | 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 90.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 3 | 95.0 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 225 to 240 | °C | |
| Middle Temperature | 230 to 260 | °C | |
| Front Temperature | 230 to 260 | °C | |
| Nozzle Temperature | 230 to 260 | °C | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.200 to 0.800 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYCOA Polyamide 2011 | Nycoa (Nylon Corporation of America) | Nylon+TPE | NYCOA Polyamide |
| BMC 350 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Fluon® PTFE PA3540LT | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| Karina RED PVC COMPOUND -E 780-42/179-A-IS (C800) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® POM HO TL20 BN042 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |