DuraStar™ DS1110UVI
| Category: | Polyester, TP , Thermoplastic Polyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | DuraStar™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9yNGv0_DuraStar-DS1110UVI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Durastar™ DS1110UVI polymer, contains an ultraviolet light stabilization package. It is recommended for indoor applications requiring enhanced color stability upon extended exposure to fluorescent light. It has excellent appearance and is nearly water-clear. Its other most outstanding features are chemical resistance and excellent processing characteristics. Easy to process, it flows readily, fills intricate molds, contains a mold release, and is well suited for thick-wall applications. This product is certified to ANSI/NSF Standard 51. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| 23°C | 1.19 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 103 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1800 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 47.0 | MPa | ASTM D638, ISO 527-2 |
| Break, 23°C | 51.0 | MPa | ASTM D638 |
| Break, 23°C | 46.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 5.0 | % | ASTM D638 |
| Yield, 23°C | 4.0 | % | ISO 527-2 |
| Break, 23°C | 300 | % | ASTM D638 |
| Break, 23°C | 200 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2000 | MPa | ASTM D790 |
| 23°C | 1850 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 65.0 | MPa | ISO 178 |
| Yield, 23°C | 69.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 40 | J/m | ASTM D256 |
| 23°C | 80 | J/m | ASTM D256 |
| -40°C | 4.8 | kJ/m² | ISO 180 |
| 23°C | 7.8 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D4812 | ||
| -40°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact | |||
| -40°C, Energy at Peak Load | 48.0 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 42.0 | J | ASTM D3763 |
| -40°C, Energy to Peak Force | 52.6 | J | ISO 6603-2 |
| 23°C, Energy to Peak Force | 58.7 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 75.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 72.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 66.0 | °C | ISO 75-2/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | ASTM D1003 | ||
| Total | 91.0 | % | |
| Regular | 89.0 | % | |
| Haze | 0.30 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 280 | °C | |
| Mold Temperature | 15.0 to 30.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREN PH 21 B 70 | SILON s.ro | PP Homopolymer | TABOREN |
| Nycal™ 1820T3 Bk-1 | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| ASTALAC™ ABS DM | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| Karina CLEAR PVC COMPOUND 60/207-DA-ATB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PENTAMID AB S GV50 H black | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |