ASTALAC™ ABS MGP35 is a high flow, medium impact general purpose ABS injection moulding grade offering an excellent balance of impact toughness, product rigidity, heat resistance and easy mouldability. Applications include general purpose mouldings including thin wall sections and long flow paths. Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS MGP35UV ]. |
General Information | |
---|---|
Features |
|
Uses |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
220°C/10.0 kg | 34 | g/10 min | |
230°C/3.8 kg | 10 | g/10 min | |
Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength 1(3.20 mm) | 38.0 | MPa | ASTM D638 |
Tensile Elongation 2(Break, 3.20 mm) | 30 | % | ASTM D638 |
Flexural Modulus 3(3.20 mm) | 2150 | MPa | ASTM D790 |
Flexural Strength 4(3.20 mm) | 65.0 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (3.20 mm) | 250 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load | ASTM D648 | ||
1.8 MPa, Unannealed, 3.20 mm | 75.0 | °C | |
1.8 MPa, Unannealed, 6.40 mm | 79.0 | °C | |
1.8 MPa, Unannealed, 12.7 mm | 87.0 | °C | |
Vicat Softening Temperature | 103 | °C | ASTM D1525 5 |
CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
Flammability | Nominal Value | Unit | Test Method |
---|---|---|---|
Flame Rating (1.60 mm) | HB | UL 94 | |
Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
Injection | Nominal Value | Unit | |
---|---|---|---|
Drying Temperature | 85.0 to 90.0 | °C | |
Drying Time | 3.0 to 6.0 | hr | |
Rear Temperature | 205 to 225 | °C | |
Middle Temperature | 215 to 235 | °C | |
Front Temperature | 225 to 245 | °C | |
Processing (Melt) Temp | 220 to 250 | °C | |
Mold Temperature | 40.0 to 70.0 | °C | |
Injection Pressure | 60.0 to 140 | MPa | |
Injection Rate | Moderate | ||
Back Pressure | 0.100 to 0.500 | MPa | |
Screw Speed | 40 to 60 | rpm | |
Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
Note Message | |
---|---|
1 . | 5.0 mm/min |
2 . | 5.0 mm/min |
3 . | 1.3 mm/min |
4 . | 1.3 mm/min |
5 . | Loading 1 (10 N) |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Synthos EPS® 0514FR/CZ | Synthos S.A. | PS (EPS) | Synthos EPS® |
Moplen HP740M | LyondellBasell Industries | PP Homopolymer | Moplen |
BP RPP 2012 TR BLK | Buckeye Polymers, Inc. | PP, Unspecified | BP |
Sumikon® PM-9630 (Type: JK Black) | SBHPP | Phenolic | Sumikon® |
Sylvin 8707-84 Brown 7339 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |