Abstron AN-312
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Bhansali Engineering Polymers Limited |
| Trademark: | Abstron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9xApHs_Abstron-AN-312.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ABS-Polycarbonate alloy with Flame Retardancy, general purpose FR-ABS and Sheet Extrusion Grade with FR feature.Cleck heare 94 V0 and V2 specifications. Some of the grades are UL certified |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 50 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 39.2 | MPa | ASTM D638 |
| Flexural Modulus (6.40 mm) | 1770 | MPa | ASTM D790 |
| Flexural Strength (Yield, 6.40 mm) | 53.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 3.20 mm | 200 | J/m | ASTM D256 |
| 6.40 mm | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 88.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 98.0 | °C | ASTM D1525 2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-0 | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 95.0 | °C | |
| Drying Time | 5.0 - 7.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Cylinder Zone 1 Temp. | 150 - 210 | °C |
| Extrusion instructions |
|---|
| Drying Time (Tray Oven): 5 to 7 hrDrying Time (Hopper Dryers): 4 to 5 hrDrying Time (Dry Air Ovens): 3 to 4 hr |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | 标准 B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAMAT 168A | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| Axiall PVC 7941 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Celcon® UV270Z | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Daelim Po1y® PH-480 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| POLIMAXX 1125NA | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |