RAMTOUGH RZ310G6
| Category: | PC , Polycarbonate |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMTOUGH |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9w9VcA_RAMTOUGH-RZ310G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GLASS-FIBER REINFORCED POLYCARBONTE FOR INJECTION MUOLDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 3.5 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.20 - 0.30 | % | ASTM D955 |
| -- | 0.20 - 0.30 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 0.070 | % | ASTM D570 |
| Saturated, 23°C | 0.070 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 120 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 195 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C | 13 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 147 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 139 | °C | ASTM D648, ISO 75-2/A |
| Thermal Conductivity | 0.24 | W/m/K | ASTM C177, DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Dielectric Strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.30 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Processing (Melt) Temp | 270 - 310 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 70.0 - 107 | MPa | |
| Holding Pressure | 35.0 - 85.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bluestar Epoxy E-52D | Bluestar New Chemical Materials Co. Ltd | Epoxy | Bluestar Epoxy |
| Diakon® CLH952LX | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| HIDEN® P601 KUBL | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |
| Lapex R G/10 | LATI S.p.A. | PPSU | Lapex |
| LNP™ COLORCOMP™ A1000H compound | SABIC Innovative Plastics | ABS | LNP™ COLORCOMP™ |