Formolene® HP3902
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation, U.S.A. |
| Trademark: | Formolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9ucPRh_Formolene-HP3902.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Formolene® HP3902 is a high performance copolymer that is designed for pressure pipe and conduit applications. It has outstanding pipe ring ESCR and it incorporates a UV stabilizer. Formolene® HP3902 meets all requirements of ASTM D4976 - PE 225. When blended with the approved color concentrates, Formolene® HP3902 has a cell class of 234373E per ASTM D3350-05, is listed by PPI as a PE2708 material with HDB's of 1,250 psi @ 73°F and 1,000 psi @ 140°F, meets the requirements of CAN/CSA Standard B137.4-02 for gas pipe and NSF Standard 14/61 for use with potable water. Formolene® HP3902 also qualifies as a PE2406 material under the old ASTM D3350-02a and PPI standards. Formolene® HP3902 also qualifies as a PE80 material per ISO 9080. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.939 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.20 | g/10 min | |
| 190°C/21.6 kg | 20 | g/10 min | |
| Environmental Stress-Cracking Resistance | |||
| 100% Igepal, Compression Molded, F50 | > 5000 | hr | ASTM D1693A |
| 100% Igepal, Compression Molded, F50 | > 5000 | hr | ASTM D1693B |
| 100% Igepal, Compression Molded, F50 | > 5000 | hr | ASTM D1693C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, Compression Molded | 19.3 | MPa | |
| Break, Compression Molded | 33.1 | MPa | |
| Tensile Elongation 2(Break, Compression Molded) | > 500 | % | ASTM D638 |
| Flexural Modulus | |||
| Compression Molded | 621 | MPa | ASTM D3350 |
| Compression Molded | 758 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -90.0 | °C | ASTM D746 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| PENT - slow crack growth | < 1000 | hr | ASTM F1473 |
| Note Message | |
|---|---|
| 1 . | Type IV, 51 mm/min |
| 2 . | Type IV, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 21T3 V25 | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Adsyl 5 C 33 F | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| Lucent TPO TPO-20NBS | Lucent Polymers, Inc. | Polyolefin, Unspecified | Lucent TPO |
| Plaslube® ABS 8004 | Techmer Engineered Solutions | ABS | Plaslube® |
| LubriOne™ NN-000/20T NATURAL | PolyOne Corporation | Nylon 66 | LubriOne™ |