Pearlbond™ 101
| Category: | TPU-Capro , Thermoplastic Polyurethane Elastomer (Polycaprolactone) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlbond™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9uVqGT_Pearlbond-101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pearlbond® 101 is a linear, polycaprolactone-based polyurethane, supplied in form of small white granules, which combines a very high crystallization rate with a very high thermoplasticity level. It is used for Hot Melt adhesives. Pearlbond® 101 is mainly used for making heat-sealable fabrics (thermobonding), obtained by coating processes such as scattering or dot-coating (powder or paste). In all cases, the product is previously ground into powder, by cryogenic grinding. The particle size of the powder will depend on the application technique to be used. Pearlbond® 101 is used for textile coating for making shoe-stiffeners (toe puffs & counters), by extrusion or sintering process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (20°C) | 1.19 | g/cm³ | ISO 2781 |
| Melt Mass-Flow Rate (MFR) (170°C/2.16 kg) | 30 to 60 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 51 | ISO 868 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 63.0 to 67.0 | °C | Internal Method |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity 1(160°C) | 380 | Pa·s | ISO 1133 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Crystallization Rate | Very High | Internal Method | |
| Softening Range | 55 to 60 | °C | Internal Method |
| Thermoplasticity | Very High | Internal Method |
| Note Message | |
|---|---|
| 1 . | 2.16 Kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 4501 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| TOTAL Polypropylene PPC 7810 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Formolene® 5181K | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| IROGRAN® A 85 P 4394 | Huntsman Corporation | TPU-Polyether | IROGRAN® |
| Durez® 37071 | SBHPP | Phenolic | Durez® |