Sarlink® TPE AB-1241DN
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9tfxqh_Sarlink-TPE-AB-1241DN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE AB-1241DN is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Sarlink®The typical application field of TPE AB-1241DN is: automobile industry |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Vertical flow direction : 23°C, 48 hours | 1.1 | % | ISO 2577 |
| Flow direction : 23°C, 48 hours | 1.1 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 10 sec) | 41 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| 23°C | 66.0 | MPa | ISO 527-2 |
| 85°C | 19.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, -35°C | 24.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 19.9 | MPa | ISO 527-2 |
| Fracture, 85°C | 5.20 | MPa | ISO 527-2 |
| 100% strain, -35 c | 16.3 | MPa | ISO 527-2 |
| 100% strain, 23°C | 7.80 | MPa | ISO 527-2 |
| 100% strain, 85°C | 0.400 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Fracture, -35°C | 450 | % | ISO 527-2 |
| Fracture, 23°C | 700 | % | ISO 527-2 |
| Fracture, 85°C | > 600 | % | ISO 527-2 |
| Flexural Modulus | ISO 178 | ||
| 23°C | 149 | MPa | ISO 178 |
| 85°C | 65.6 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| -35°C | 130 | kN/m | ISO 34-1 |
| 23°C | 80 | kN/m | ISO 34-1 |
| 85°C 1 | 27 | kN/m | ISO 34-1 |
| 85°C 2 | 46 | kN/m | ISO 34-1 |
| 85°C 3 | 40 | kN/m | ISO 34-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Annealed) | 43.9 | °C | ISO 75-2/B |
| Glass Transition Temperature | -60.0 | °C | DSC |
| Melting Temperature (DSC) | 159 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | 83 | mm/min | FMVSS 302 |
| Additional Information |
|---|
| 雾化，3小时，100C = 97% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | Method A, Pant-Shaped Specimen |
| 2 . | Method B, right-angle specimen (without cut) |
| 3 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR PP FR 7C11 | PolyOne Corporation | PP, Unspecified | Maxxam™ FR |
| Next Nylon 66 Prime Series PG15-01BL | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Comai 712-1 UV | Comai Ltda | PP, Unspecified | Comai |
| Forprene® 6NM001A60 | SO.F.TER. SPA | TPV | Forprene® |
| Pebax® Rnew 70R53 SP 01 | Arkema | PEBA-Ether | Pebax® Rnew |