Cevian®-V 770
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Cevian®-V |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9tbW8M_Cevian--V-770.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cevian®-V 770 is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by extrusion and is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 7.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 - 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 40.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 14 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 102 | °C | ISO 306/A50 |
| -- | 92.0 | °C | ISO 306/B50 |
| -- | 94.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Mold Shrinkage, ISO 294, was tested in accordance with ISO 2577. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 - 200 | °C | |
| Middle Temperature | 200 - 220 | °C | |
| Front Temperature | 220 - 240 | °C | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 48.9 - 60.0 | °C | |
| Injection Pressure | 34.5 - 103 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.689 - 2.07 | MPa | |
| Screw Speed | 60 - 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QAMAR FC21HS | SPDC Ltd. | LLDPE | QAMAR |
| STYRON™ 470 | Trinseo | PS (HIPS) | STYRON™ |
| Moplen HP400N | LyondellBasell Industries | PP Homopolymer | Moplen |
| TOTAL Polypropylene PPR 3727WZ | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| TOTAL Polyethylene XSene® HDPE XRC 20 B | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |