Maxxam™ NT-818.G002-8000
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9t4mSv_Maxxam-NT-818-G002-8000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Specific Volume | 0.910 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 68.9 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 4620 | MPa | ASTM D790 |
| Flexural Strength | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 64 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.18 mm) | 160 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ALL) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 16.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND 2200 | POLY GIN | PC | MARCOBLEND |
| Unilex™ UP 8020 | United Polychem | PP Homopolymer | Unilex™ |
| Nypol® PA B3 D40 NTLA010 NT394 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Latilub 66-01M G/50 | LATI S.p.A. | Nylon 66 | Latilub |
| Karina IVORY PVC COMPOUND 858-35/1-E-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |