POLYFLAM® RABS 90350 UV5
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9stx5d_POLYFLAM-RABS-90350-UV5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% mineral filled ABS grade without PBDE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.80 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 37.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 2.5 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.5 | kJ/m² | ISO 179/1eA |
| 23°C | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 75 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 92.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 77.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 102 | °C | ISO 306/A50 |
| -- | 93.0 | °C | ISO 306/B50 |
| Ball Pressure Test (85°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | UL 746 | ||
| 1.50 mm | 60.0 | °C | UL 746 |
| 3.00 mm | 60.0 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 1.50 mm | 60.0 | °C | UL 746 |
| 3.00 mm | 60.0 | °C | UL 746 |
| RTI | UL 746 | ||
| 1.50 mm | 60.0 | °C | UL 746 |
| 3.00 mm | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | ISO 3795 | ||
| 1.50mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| 3.00mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 1.50 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 3.00 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 675 | °C | IEC 60695-2-13 |
| 3.00 mm | 700 | °C | IEC 60695-2-13 |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 220 | °C | |
| Middle Temperature | 230 | °C | |
| Front Temperature | 240 | °C | |
| Nozzle Temperature | 240 | °C | |
| Processing (Melt) Temp | 220 - 240 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Pressure | 80.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 40.0 - 90.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Cushion | < 5.00 | mm | |
| Screw Speed | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 154 HI UV | RTP Company | PP Copolymer | RTP |
| TECHNO ABS 77 K4 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| ZYLAR® 245 | INEOS Styrolution Group GmbH | MMBS | ZYLAR® |
| Karina BLACK PVC COMPOUND 750-48/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Panlite® GN-3610ZL | TEIJIN LIMITED | PC | Panlite® |