ULTEM™ ATX200F resin
| Category: | PEI+PCE , Polyether Imide + PCE |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9sZN1Q_ULTEMATX200Fresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow Polyetherimide blend. ECO Conforming, UL94 V0 Listing. US FDA Food Contact compliant. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 24 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 96.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 70 | % | ASTM D638 |
| Flexural Modulus 3(100 mm Span) | 3170 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 100 mm Span) | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 2100 | J/m | ASTM D4812 |
| Reverse Notch Izod Impact (3.20 mm) | 2700 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 191 | °C | ASTM D648 |
| RTI Elec | 115 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI | 115 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.762 mm | V-2 | UL 94 | |
| 1.50 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 10 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 338 - 360 | °C | |
| Middle Temperature | 343 - 366 | °C | |
| Front Temperature | 349 - 371 | °C | |
| Nozzle Temperature | 349 - 371 | °C | |
| Processing (Melt) Temp | 349 - 371 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | 2.6 mm/min |
| 4 . | 2.6 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 881 TFE 10 | RTP Company | Acetal (POM) Copolymer | RTP |
| SCHULAMID® 66 RBL 2500 BLACK | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Hifax TYC 1123X | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| LNP™ LUBRICOMP™ DEL36P compound | SABIC Innovative Plastics Europe | PC | LNP™ LUBRICOMP™ |
| Plexiglas® V920 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |